304N low temperature stainless steel sheet is a type of austenitic stainless steel that is often used in low temperature applications. This particular stainless steel sheet is made up of 18% chromium, 8% nickel, and 0.3% nitrogen. The nitrogen content in this stainless steel sheet provides an excellent increase in strength and corrosion resistance.

 

Chemical Composition of 304N Low Temperature Stainless Steel Sheet

 

The chemical composition of 304N low temperature stainless steel sheet is as follows:

 

- Chromium: 18%

- Nickel: 8%

- Nitrogen: 0.3%

- Carbon: 0.08%

- Silicon: 1%

- Manganese: 2%

- Phosphorus: 0.045%

- Sulphur: 0.03%

 

Mechanical Properties of 304N Low Temperature Stainless Steel Sheet

 

The mechanical properties of 304N low temperature stainless steel sheet are as follows:

 

- Tensile strength: 590 MPa

- Yield strength: 285 MPa

- Elongation: 55%

- Hardness: 201 HB

 

Applications of 304N Low Temperature Stainless Steel Sheet

 

304N low temperature stainless steel sheet is commonly used in various low temperature applications such as cryogenics, food processing equipment, and medical equipment. Its excellent strength and corrosion resistance make it an ideal choice for such applications. Additionally, it is easy to form and weld which makes it a cost-effective material for manufacturing.

 

Supply of 304N Low Temperature Stainless Steel Sheet

 

304N low temperature stainless steel sheet can be easily sourced from reliable suppliers worldwide. Some notable suppliers include ThyssenKrupp, Outokumpu, and Sandvik. These suppliers offer quality products at competitive prices and with reliable delivery times.

 

Conclusion

 

In conclusion, 304N low temperature stainless steel sheet is a valuable material that possesses excellent strength and corrosion resistance properties. Its chemical composition, mechanical properties, and applications make it a suitable choice for various industries. With reliable suppliers offering quality products, it is readily available for use in manufacturing.