HARDOX 500 WEAR RESISTANT STEEL PLATE- TJC STEEL.
 HARDOX 500 is a kind of Brinell hardness 500HB wear-resistant steel plate, mainly used in anti-wear [TJC STEEL]conditions.

"1" Sweden SSAB welding wear-resistant steel

"2" HARDOX500 Handa wear-resistant steel applications: crusher, screen plate, feeder, feeding funnel, elevator, blade plate, conveyor, bucket, knife plate, gear, sprocket and so on.

"3" HARDOX500 Handa wear-resistant[TJC STEEL] steel is: "Fine-grained steel". "4" HARDOX500 wear-resistant steel hardness: 4-32mm =470-530HBW, 32-80MM=450-540HBW..

"5" HARDOX500 Handa wear-resistant steel mechanical properties: yield strength Re=1250MPa(not mandatory). [TJC STEEL]Elongation A5=10% (typical value of 20 mm thickness steel plate).

"6" HARDOX 500 Handa wear-resistant steel impact toughness: test temperature: -40 (-40F) ℃. Impact power Charpy-V longitudinal =45J (typical value of 20 mm thick steel plate). Impact energy Charpy-V transverse 27J/+20℃.

"7" HARDOX 500 Handa wear-resistant[TJC STEEL] steel delivery status: quenched.

"8" HARDOX500 Hander wear-resistant steel implementation standard: EN 10 204-3.1.

"9" HARDOX500 Product Application:

Due to the combination of high hardness, high strength and high toughness, HARDOX is obviously the [TJC STEEL]ideal choice for those occasions where the wear is severe. The high wear resistance of the steel plate extends the service life of the body of the dump truck, the bucket of the excavator, the crusher and similar equipment.

The hardness of the steel plate is obtained through an effective quenching process on our water quenching line. This method can obtain a high hardness, while maintaining a [TJC STEEL]low alloy composition in the steel. The resulting wear-resistant plate is easy to machine, bend and weld.

 

Product Category

HARDOX wear-resistant steel plate is divided into: HARDOX wear-resistant up to 400, HARDOX wear-resistant up to 450, HARDOX wear-resistant up to 500;

HARDOX has reached 550, HARDOX [TJC STEEL]has reached 600 and HARDOX has reached HiTuf. This means that you can always find a HARDOX steel plate that meets your specific needs.

The HARDOX Solder 400 and HARDOX Solder 450 are versatile wear plates. Due to its high toughness, good bending and welding properties, it can also be used for bearing purposes in some applications.

The HARDOX 500 is a bendable and weldable wear-resistant plate that can be used in applications that require higher wear resistance.

HARDOX 550 is a wear-resistant [TJC STEEL]steel plate with an average hardness of 550HBW, and its toughness is the same as HARDOX 500, which is used in high-wear applications. It is mainly aimed at users and manufacturers using high manganese steel castings or wear resistant steel plates with Brinell hardness of 500, when upgrading from HARDOX 500 steel plate to this product, the Brinell hardness is increased by 50 units, extending the wear life without losing the toughness of the steel plate. Find out more: HARDOX Hardened up to 550, HARDOX Hardened up to 550 in the Workshop Uses: HARDOX Hardened up to 500 steel plates typically have a hardness of 500 HBW, making them able to withstand severe wear. It is ideal for [TJC STEEL]working in high-wear environments, such as high-strength ores and corrosive materials.

HARDOX 600 is the hardest wear resistant steel in the world with a hardness of 600HBW. It is generally used in extremely severe wear situations, and is mainly used to replace cast steel, chromium alloy cast iron and surface hardened metals. Despite its high hardness, we are able to machine, weld and cut it. Although HARDOX has a very high hardness of up to 600, it still has a fairly high impact toughness.

HARDOX HiTuf is a wear-resistant steel plate with extremely high toughness and excellent cracking [TJC STEEL]resistance. HARDOX HiTuf has an average hardness of 350HBW and is mainly used in important components requiring extremely high wear and crack resistance.