5086 aluminum alloy is mainly used in ships, automobiles and aircraft plate weldable parts, etc.

Chinese name 5086 aluminum alloy[TJC STEEL] standard: GB/T 4437.1-2000 Aluminum Al: residual silicon Si: ≤0.40 copper Cu: ≤0.10

 

Overview of 5086 Aluminium Alloy

Aluminum-magnesium alloy and aluminum-manganese alloy are collectively referred to as anti-rust aluminum, because the alloy [TJC STEEL]composition between them can increase their anti-corrosion properties. The representative of aluminum-manganese alloy is 3003,3004,3105. According to the magnesium alloy content, the order is 5005, 5252, 5251, 5050, 5052, 5754, 5083, 5056, 5086 and so on. 5086 aluminum plate typical use: for the need to have high corrosion resistance, good weldability and medium strength occasions, such as the need for strict fire pressure vessels, refrigeration devices, TV towers, installation of exploration equipment, transportation equipment, missile parts, armor, etc.

5086 aluminum plate supply status: O, H112,[TJC STEEL] H116, H111, H321, H32, H36, H38

 

Chemical Composition for 5086 Aluminium Alloy

Silicon :0.00 to 0.40

Iron Fe: 0.000 ~ 0.500

Copper Cu:0.00 to 0.10

Magnesium Mg: 3.5 ~ 4.5

Zinc-zn: ≤0.25

Manganese Mn: 0.20 ~ 0.7

Ti: ≤0.15

Chromium Cr: 0.05 ~ 0.25[TJC STEEL]

Note: Single :≤0.05; Total :≤0.15

 

Mechanical Property of 5086 Aluminium Alloy

Tensile strength σb (MPa) : ≥240

Conditional yield strength σ0.2 (MPa) : ≥95

Elongation δ10 (%) : ≥10

Elongation δ5 (%) : ≥12

Note: longitudinal mechanical properties of pipe at room temperature

Sample size: all wall thickness[TJC STEEL]

State: Aluminum and aluminum alloy hot extrusion seamless round tube (H112 state)