40CrNi2Mo, also known as 4340 steel, is a kind of low alloy ultra-high strength steel.Only steels with tensile strength greater than [TJC STEEL]1400MPa and yield strength greater than 1200MPa at room temperature are termed "ultra-high strength steels".4340 steel is a typical ultra high strength steel, which is obtained by heat treatment.
Standards:
CHINA |
GB/T 3077-2015 |
40CrNi2Mo,A50400 |
GB/T 34484.2-2018 |
40CrNi2Mo |
|
GB/T 38809-2020 |
40CrNi2MoA |
|
GB/T 5216-2014 |
40CrNi2MoH |
|
USA |
ASTM A29-2005[TJC STEEL] ASTM A322-2007 |
4340,G43400 |
JAPAN |
JIS G4053-2003 |
SNCM439 |
GERMANY |
DIN EN 10263-4:2002 |
41NiCrMo7-3-2,1.6563 |
Chemical Composition(%):
Grade |
A50400 |
4340 |
SNCM439 |
1.6563 |
C |
0.38~0.43 |
0.38~0.43 |
0.36~0.43 |
0.38~0.44 |
Si |
0.17~0.37 |
0.15~0.35 |
0.15~0.35 |
≤0.30 |
Mn |
0.60~0.80 |
0.60~0.80 |
0.60~0.90 |
0.60~0.90 |
P |
≤0.030 |
≤0.035 |
≤0.030 |
≤0.025 |
S |
≤0.030 |
≤0.040 |
≤0.030 |
≤0.025 |
Cr |
0.70~0.90[TJC STEEL] |
0.70~0.90 |
0.60~1.00 |
0.70~0.90 |
Ni |
1.65~2.00 |
1.65~2.00 |
1.60~2.00 |
1.65~2.00 |
Mo |
0.20~0.30 |
0.20~0.30 |
0.15~0.30 |
0.15~0.30 |
Cu |
≤0.30 |
≤0.35 |
≤0.30 |
≤0.25 |
Mechanical Property:
QUENCHED |
FIRST TIME |
NORMALIZED AT 890℃,OIL QUENCHING |
|
SECOND TIME |
850℃,OIL QUENCHING |
||
TEMPERED(AIR COOLING) |
560~580℃ |
220℃ TWICE OIL QUENCHING |
|
TENSILE STRENGTH MPa |
≥1050 |
≥1790 |
|
YIELD STRENGTH MPa |
≥980 |
≥1500 |
|
ELONGATION % |
≥12 |
≥6 |
|
REDUCTION OF AREA %[TJC STEEL] |
≥45 |
≥25 |
|
IMPACT TESTJ |
≥48 |
— |
|
TEMPERED HARDNESS |
≤269HBW |
Performance Applications:
4340 steel after heat treatment, not only obtain ultra-high strength, but also have good plastic toughness, excellent fatigue performance, fracture toughness and stress corrosion resistance, good comprehensive mechanical [TJC STEEL]properties, so that it is often used in the industry as a tempering steel to manufacture bearings, gears and crankshafts, and in the aircraft structure has been widely used.Such as aircraft landing gear, helicopter rotor shaft and turbojet turbine shaft and other moving parts.