12Cr21Ni5Ti (1Cr21Ni5Ti) is a dual-phase stainless steel developed in the former Soviet Union.The steel is designed to save nickel instead of 1Cr18Ni9Ti, [TJC STEEL]but has better mechanical properties than the latter, especially higher strength.

 

Component specification(GB/T 20878-2007)

C

0.09~0.14

Ni

4.80~5.80

Si

≤0.80

Cr

20.00~22.00

Mn

≤0.80

Ti

5(C-0.02)~0.80

P

≤0.035[TJC STEEL]

S

≤0.030

 

Corrosion Resistance

12Cr21Ni5Ti steel has good corrosion resistance in oxidizing acid and organic acid, and can be used instead of 1Cr18Ni9Ti steel.Because the steel contains stabilized element titanium and is a two-phase structure, there is [TJC STEEL]generally no tendency of intergranular corrosion.

 

Corrosion Rate Under Three Media Conditions

ambient condition

T

testing time

corrosion rate

 

 

 

mm/a

65%HNO3

boiling

96~192h

0.5

10% oxalic acid

boiling

96~192h

0.01

oxalic acid(10copies)

boiling

22h[TJC STEEL]

5.6~7.1

+NaCl(1copies)

 

 

 

 

Welding Performance:

12Cr21Ni5Ti steel has good weldability and can be welded by various methods.The performance of the weld metal is similar to that of the base metal when the welding filler material with the same composition as the base metal is[TJC STEEL] used.For manual welding (SMAW), an 18-8 type austenitic stainless steel electrode without a stable element can also be used.

 

Cold And Hot Working Properties:

The cold and hot working properties of 12Cr21Ni5Ti steel are good.Thermal processing temperature range 1050 ~ 800℃.The best thermoplasticity occurs at 950 ~ 1050℃.Due to the higher yield strength, cold processing, especially pipe flares and sheet deep drawing are slightly worse than austenitic stainless steel, [TJC STEEL]but once the yield deformation, you can be smooth processing.

 

Applications:

12Cr21Ni5Ti steel can be used to replace 1Cr18Ni9Ti steel, mostly used to manufacture both oxidation resistance acid corrosion, and requires higher strength of equipment or components, used in the aviation industry for the [TJC STEEL]manufacture of aircraft engine shell and rocket engine combustion outdoor wall.