06Cr13 (0Cr13),410S,SUS410S,1.4000 Martensitic (Ferrite) Stainless Steel- TJC STEEL.

Favorite | Set Home

Products Category

Copper Alloy Plate

Pressure Vessel and Boiler Steel Plate

Aluminum Alloy Plate

High Strength Steel Plate

Copper Alloy Pipe/ Tube

Wear-Resistant Steel Plate

Marine and Offshore Steel Plate

Carbon Structural Steel Plate

Weather Resistant Steel Plate

Low Alloy Steel Plate

Stainless Steel Plate

Steel Section

Steel Pipe

Stainless Steel Section

Stainless Steel Tube

Tel: +86-371-86107816
Fax: +86-371-63797816
E-mail: [email protected]
Add: Fortune Plaza, Zhengzhou, Henan, China
Skype: tjccarl

Link

06Cr13 (0Cr13),410S,SUS410S,1.4000 Martensitic (Ferrite) Stainless Steel- TJC STEEL.

06Cr13, the American standard 410S, is the lowest carbon content in the Cr13 martensitic stainless steel.Due to the microstructure of[TJC STEEL] the matrix under annealing condition, it is also classified as ferritic stainless steel in a few standards.

Standard Control

CHINA	GB/T 20878-2007	S41008	06Cr13 （0Cr13）
	GB/T 24511-2009	S11306
AMERICA	ASTM A240-15a	S41008,410S
JAPAN	JIS G 4304:2005	SUS410S
GERMANY	DIN EN 10088-2:1995[TJC STEEL]	X6Cr13,1.4000

Component Specification

GRADE	06Cr13*	410S	SUS410S	1.4000
C	≤0.08	≤0.08	≤0.08	≤0.08
Si	≤1.00	≤1.00	≤1.00	≤1.00
Mn	≤1.00	≤1.00[TJC STEEL]	≤1.00	≤1.00
P	≤0.040	≤0.040	≤0.040	≤0.040
S	≤0.030	≤0.030	≤0.030	≤0.015
Cr	11.5~13.5	11.5~13.5	11.5~13.5	12.0~14.0
Ni	(≤0.60)	≤0.60	(≤0.60)	—

*：S41008 is listed in the table, while S11306 is slightly different in composition.

Mechanical Property

Density（g/cm3）20℃[TJC STEEL]		7.75
Specific heat [kJ/(kg·K)] 0~100℃		0.46
Heat conductivity [W/(m·K)]	100℃	25.0
coefficient of linear expansion（10-6/K）	0~100℃	10.6
	0~500℃	12.0
specific resistance（Ω·mm2/m）20℃		0.60
longitudinal modulus of elasticity（kN/mm2）20℃		220
magnetism		Y

Mechanical Property

Dimensions of sample hairs（mm）		≤75
heat treating regime	anneal[TJC STEEL]	800 ~ 900 ℃ slow cooling Or about 750℃ fast cooling
	quench	950 ~ 1000 ℃ cold oil
	temper	700~750℃cold oil
Mechanical properties (quenching + tempering)	Specified non-proportionality Extension strength MPa	≥345
	strength of extension MPa	≥490
	Percentage elongation after fracture %	≥24
	Percentagereduction of area; reduction of area	≥60
The hardness of delivery HBW	anneal	≤183

Material Characteristics:

(1) The corrosion resistance and corrosion resistance are similar to 1Cr13 (410) and better, in low concentration of mild organic and [TJC STEEL]inorganic acid, alkali and some chemical conditions have corrosion resistance.

(2) Good oxidation resistance, sustainable use in 705℃ environment.

(3) good plastic toughness, easy to be formed by rotation, bending and rolling.

(4) It can be welded by common fusion and resistance technology.

Applications:

The main product form [TJC STEEL]is plate, used for structural parts such as automobile muffler and exhaust system components, but also widely used in containers, heat exchangers, underground pipes, etc.