Common Preparation Methods:
Arc Melting - Casting Process
After melting pure molybdenum by electric arc, certain Ti, Zr and other alloying elements are added according to the percentage of weight, and then TZM alloy is obtained by conventional casting method.
Powder Metallurgy
After mixing high pure molybdenum powder with TiH2 powder, ZrH2 powder and graphite powder in a uniform proportion, it was formed by isostatic pressing and then sintered at high temperature in a protective atmosphere to obtain TZM blank.The blank is then hot-rolled (forging) at high temperature, annealed at high [TJC STEEL]temperature, annealed at medium temperature (forging), relieved of stress at medium temperature, and then rolled (forging) at warm temperature, and finally TZM finished material is obtained.
Standaards:
CHINA |
YS/T 660-2007 GB/T 17792-2014 GB/T 3816-2017 |
TZM |
AMERICA |
ASTM B386-2003 ASTM B387-2010 |
363,364[TJC STEEL] |
Chemical Composition(%)
GRADE |
TZM |
363 |
364 |
Ti |
0.40~0.55 |
0.40~0.55 |
0.40~0.55 |
Zr |
0.06~0.12 |
0.06~0.12 |
0.06~0.12 |
Mo |
REST |
REST |
REST |
C |
0.01~0.04 |
0.01~0.03 |
0.01~0.04 |
Fe |
≤0.010 |
≤0.010 |
≤0.010 |
Ni |
≤0.005 |
≤0.002 |
≤0.005 |
Si |
≤0.005 |
≤0.010 |
≤0.005 |
N |
≤0.003 |
≤0.002[TJC STEEL] |
≤0.002 |
O |
≤0.080 |
≤0.003 |
≤0.030 |
B |
(0.02) |
— |
— |
Performance Characteristics
TZM alloy has the characteristics of high melting point, high strength, high elastic modulus, small linear expansion coefficient, low vapor [TJC STEEL]pressure, good electrical and thermal conductivity, and strong corrosion resistance.TZM has excellent thermal shock resistance and thermal fatigue resistance in an environment above 1000℃.
Applications
Because of excellent high temperature strength, low temperature ductility and good welding performance, TZM alloy is widely used in [TJC STEEL]industry for the processing of high temperature structural materials and die materials, and because of its high melting point, string cable expansion coefficient, low vapor pressure, good conductive heat conduction the characteristic such as performance, is widely used in aerospace, military industry and high temperature structural materials, etc.