Chemical Composition for XM-19:
碳 C:≤0.06,硅 Si:≤1.0,锰 Mn:4-6,磷 P:≤0.045,硫 S:≤0.03,铬 Cr:20.5-23.5,镍 Ni:11.5-13.5,钼Mo:1.5-3.0,氮 N:0.2-0.4,[TJC STEEL]cb:0.1-0.3,钒V:0.1-0.3
Mechanical Property for XM-19:
Density :7.8 g/cm3
Melting Point :1415-1450 ℃
Minimum Mechanical Properties of XM-19 Alloys At Room Temperature:
Tensile Strength Rm N/mm2
Yield Strength RP0.2n /mm2
Elongation A5%
Brinell hardness HB
Solid Melting State 690 380 35 ≤241
Corrosion Resistance of XM-19:
UNS S20910 / XM-19 stainless steel has excellent general corrosion resistance and is superior in many respects to 316/316L and 317/317L.
Annealing conditions at 1950°F (1066°C) provide sufficient corrosion resistance for many applications while providing high [TJC STEEL]strength.When using materials in welded or highly corrosive medium, the annealing condition of 2050°F (1121°C) shall be selected.Materials under high strength cold working conditions are usually used for bolting and shafting connections, but there are some minor compromises in corrosion resistance compared to annealing conditions in some environments.
UNS S20910 / XM-19 stainless steel (annealed) is more resistant to crevice corrosion (e.g., crevice corrosion) than type 316/316L.As [TJC STEEL]with most austenitic stainless steels (such as 304 and 316), XM-19 steel may undergo stress corrosion cracking in an environment containing thermochloride ions.
XM - 19 Features:
Xm-19 stainless steel has a perfect combination of corrosion resistance and strength not found in any other commercial material.The corrosion resistance of this austenitic stainless steel is superior to alloys 316, 316L, 317, 317L, and the yield strength at room temperature is approximately twice that of these [TJC STEEL]alloys.In addition, the XM-19 differs from most austenitic stainless steels in its excellent mechanical properties at both high and sub-zero temperatures.
XM-19 also does not become magnetic at low temperatures.
The yield strength of the HIGH strength[TJC STEEL] (HS) XM-19 is approximately 3 times that of 316 stainless steel.
XM-19 Application Areas:
Widely used in the Marine, nuclear, chemical and oil and gas industries.