UNS N06002 is a nickel-chromium alloy with the addition of drill and tungsten. The alloy has excellent oxidation resistance[TJC STEEL] at high temperatures up to 1200℃ and can also be used in neutral and reductive atmospheres. At the same time, the alloy can resist carbonization and nitriding atmosphere.
Chemical Composition (%):
Ni:Rest;
W: 0.2-1.0;
Fe:17-22;
Mn: 1.0 Max;
C: 0.05-0.15;
Si: 1.0 Max;[TJC STEEL]
S: 0.03 Max;
Cr: 20.5-23;
Mo:8-10;
P: 0.04 Max;
Co: 0.5-2.5;
Physical Property
Density: 8.28 g/cm after;
Melting Point:1260-1355℃;
Mechanical Property[TJC STEEL]
Tensile Strength:690MPa min;
Yield Strength:276MPa min;
Elongation(%):35min;
Product Standard
N06002 Bar-ASTM B572; N06002 Plate-ASTM B435; N06002 Seamless Pipe-ASTM B622; N06002 Welded Pipe:ASTM B619;[TJC STEEL] N06002 Pipe Fitting-ASTM B626; N06002 Forged Product-ASTM B575,etc.
Product Characteristics
A. Good cold and hot processing performance;
B. With satisfactory welding performance, it can be welded by argon arc welding, seam welding, spot welding and other [TJC STEEL]methods;
C. The adhesion of surface oxides and welding slag around the weld is stronger than that of stainless steel;
Application Field
1.Industrial and aerospace turbines;
B.Spiral tubes in petrochemical furnaces;
C.Industrial furnace components (support rolls, grids, ribbons and radiation tubes);
D.High temperature gas cooled nuclear reactors;
E.Industrial and aviation[TJC STEEL] steam turbines
F.Spiral tubes in petrochemical furnaces
G.Industrial furnace components (support rolls, grids, ribbons and radiation tubes)
H.High temperature gas cooling nuclear reactors