Product Introduction

UNS N06635 is a nickel-based superalloy with a unique combination of properties. It has excellent thermal stability, low thermal expansion and excellent oxidation resistance to 2000 °F (1093 °C). In addition, the alloy has good high [TJC STEEL]temperature and thermal fatigue strength, Hastelloy S wire is a thin nickel alloy circular material, made by cold-drawn wire. Compared with ordinary stainless steel wire, it has better corrosion resistance and high temperature resistance.

 

 

Chemical Composition (%):

Alloy-S

C: 0.02 Max;

Cr: 14.5-17;

Ni:Rest;

Fe:3Max;

Mo: 14-16.5;

W:1Max;

Al: 0.1-0.5;[TJC STEEL]

La: 0.01-0.1;

Co:2Max;

Si: 0.2-0.75;

Mn: 0.3 1;

P: 0.02 Max.

S: 0.015 Max;

 

Physical Property

Density: 8.75 g/cm3;

Melting Point:1335-1380℃;

Electrical Resistivity:1.28;

Dilatation Coefficient:11.5*10E-6;

Heat Conductivity:14;

Thermal Diffusivity:3.6*10E-6;[TJC STEEL]

Specific Heat Capacity:398;

 

 

High Temperature Mechanical Properties

Test Sample Thickness:1.1-1.6MM;

Test Temperature:1093℃;

Tensile Strength Rm:110MPa min;

Yield Strength Rp:52MPa min;

Elongation A5%:46 min;[TJC STEEL]

 

 

 

 

 

Product Characteristics

1. Excellent thermal stability, low thermal expansion and excellent oxidation resistance;

2. Good high temperature[TJC STEEL] and thermal fatigue strength;

3. Maintain its strength and ductility after aging at a temperature of 427 to 871 ° C;

 

 

Application Field

 

Seals for industrial furnaces and gas[TJC STEEL] turbine engines