Product Introduction

UNS N06035 is a nickel-based alloy with a high chromium content that offers superior corrosion resistance to commercial phosphoric acid and to the mixed environments of many highly [TJC STEEL]oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid than most other nickel - and iron-based alloys. The N06035 alloy prevents the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications.

 

 

Chemical composition (%):

N06035 Alloy

Ni:Rest; Cr: 32.25-34.25; Mo: 7.6-9; Fe:≤2; Co:≤1; W: 0.6 or less. Mn: 0.5 or less; Si: 0.6 or less; C: 0.05 or less; [TJC STEEL]Al: 0.4 or less; P: 0.03 or less. S: 0.015 or less; Cu: 0.30 or less; V: 0.2 or less.

 

 

Physical Property

Density: 8.9 g/cm after;

Melting Point:1331-1361℃;[TJC STEEL]

 

Mechanical properties /MPa(Room Temperature):

Heat Treatment: Annealed;

Tensile Strength:≥586;

Yield Strength:≥241;

Elongation/A5%:≥30%;

 

Product standard

ASTM B574,ASTM B575, [TJC STEEL]ASTM B564, ASTM B619, ASTM B622, ASTM B626, ASTM B366, ASTM B462, ASTM B472.

 

Application field

● Evaporator for wet phosphoric acid production

● Pickling equipment using nitric acid and hydrofluoric acid

● caustic soda[TJC STEEL] neutralization system

● Chemical systems involving nitric acid and chloride