⑴ Introduction of Ingredients:

Implementation Standard (ASTM A182)

Elements C, Mn,[TJC STEEL] P, S, SI

MIN

MAX 0.15 2.00 0.035 0.030 1.00

The element Ni Cr Mo TI N

MIN 6 16

MAX 8 18 0.1

 

S30100 Applications and Features:

S30100 is a kind of metastable austenitic stainless steel, in a fully solid solution state, it has a complete austenitic [TJC STEEL]structure, because of its austenitic instability, when deformed by cold working, there will be deformation martensite formation, the number depends on the size of the deformation and deformation temperature. In austenitic stainless steel, S30100 is the most easy to cold deformation and strengthening of steel, through cold processing deformation can improve the strength and hardness of steel, and still maintain enough plastic toughness, S30100 has good rust resistance under atmospheric conditions, therefore, mainly in the cold processing state applied to bear higher loads, but also hope to reduce the weight of equipment and rust free equipment and components. S30100 is easy to produce work hardening when impacted by external forces, which can absorb more[TJC STEEL] collision energy, and provide more reliable protection for equipment and personnel.

S30100 applies all kinds of stamping parts, fasteners and other products requiring high strength.

 

S30100 Material Specification:

Rolled sheet 0.05mm-2.0mm, width: 20-600, forgings of various sizes and specifications. 5.5-30 Hot rolling solid solution pickling wire, disc round.

 

S30100 Room temperature Physical Properties:

Melting point: 1400-1420℃

Density: 8.0g/cm2

Specific heat capacity: 500J/Kg.K

Linear expansion coefficient: 17 10-6/K

Elastic modulus: 193GPa

Resistance: 720 ηω.m [TJC STEEL]

S30100 room temperature mechanical properties:

Sample and state: solution annealing

Implementation standard: GB1220-90

Tensile strength: ≥520MPa

Yield strength: ≥205MPa

Section shrinkage: ≥60%

Hardness: ≥200HV

 

Differences in physical properties of cold rolled rolling materials:

Implementation Standard (ASTM A666)

Test state Tensile strength Yield strength elongation Remarks

1/4H 860 515 25 No less [TJC STEEL]than

1/2H 1030 760 10 No less than

3/4H 1210 930 7 Not less than

H 1280 965 5 Not less than

EH 1550 1250

TEH 1700 1400

 

S30100 Delivery Status:

The S30100 surface can be made [TJC STEEL]of various types, such as BA/2B, 8k, etc. Wire, disc circle can be delivered according to customer requirements soft state and light pull.