Species
Alloy Structural Steel: SCM435
Implementation Standard: JIS G4053-2008
Chemical Composition of SCM435
C: 0.33 ~ 0.38 Si: 0.15 ~ 0.35
Manganese Mn: 0.60 ~ 0.90
Sulfur S: Allowable [TJC STEEL]residual content ≤0.030
Phosphorus P: Allowable residual content ≤0.030
Cr: 0.90 ~ 1.20
Nickel Ni: Permissible residual content ≤0.25
Cu Cu: Permissible residual content ≤0.30
Mo: 0.15 ~ 0.30
SCM435 Standard
SCM435 standard :SCM435 [TJC STEEL]is the Japanese standard (JIS G4053-2008) steel, the domestic corresponding steel 35CrMo
SCM435 Hardness
The hardness of SCM435 is HRC36 ~ 43, HB269 ~ 341
Mechanical Properties of SCM435
Tensile Strength (MPa) : ≥985(100)
Yield Strength σs (MPa) : ≥835(85)
Elongation δ5 (%) : ≥12
Section Shrinkage rate ψ (%) : ≥45
Impact Energy Akv (J) : ≥63
Impact Toughness αkv (J/cm²) A: 78 (8) or
Hardness: 229 hb or less
Sample Size: [TJC STEEL]sample blank size is 25mm
Heat Treatment Specification
Heat Treatment Specification: quenching 850℃, oil cooling; Tempering 550℃, water cooling, oil cooling.
Delivery Status: heat treatment (normalizing, annealing or high temperature tempering) or no heat treatment, delivery [TJC STEEL]status should be indicated in the contract. Annealing no.1 "annealing at 760±10℃, furnace cooling to 400℃ air cooling.
HB220-230
860±10℃ normalize, air cooling out of the oven.
Quenching water or oil (depending on the complexity of product type), 680-700 degrees tempering. HB<217
Quenching oil at 840±10℃ and then tempering at 470 ℃. HRC41-45
Quenching oil at 840±10℃ and then tempering at 480 ℃. HRC35-45
Tempering +tempering No.8 quenching oil at 850℃ and tempering at 510 ℃. HRC38-42
Tempering +tempering No.9 quenching oil at 850℃ and then tempering at 500 ℃. HRC40-43
Tempering +tempering [TJC STEEL]No.10 quenching oil at 850℃ and tempering at 510℃. HRC36-42
Quenching oil at 850℃ and then tempering at 560℃. HRC32-36
Oil quenching at 860℃ and tempering at 390 ℃. HRC48-52