National Standard
CHINA |
GB/T 1220-2007 |
Y10Cr17 (Y1Cr17) |
AMERICA |
ASTM A582-2005 |
S43020 430F |
JAPAN |
JIS G 4303-2005 |
SUS430F |
GERMANY |
DIN EN 10088-1:2005[TJC STEEL] |
X6CrMoS17 1.4105 |
Component Specification
GRADE |
Y10Cr17 |
430F |
SUS430F |
1.4105 |
C |
≤0.12 |
≤0.12 |
≤0.12 |
≤0.08 |
Si |
≤1.00 |
≤1.00 |
≤1.00 |
≤1.50 |
Mn |
≤1.25 |
≤1.25 |
≤1.25 |
≤1.50 |
P |
≤0.06 |
≤0.06 |
≤0.040 |
≤0.040 |
S |
≥0.15 |
≥0.15 |
≥0.15 |
0.15~0.35 |
Cr |
16.0~18.0 |
16.0~18.0 |
16.0~18.0 |
16.0~18.0 |
Mo |
(≤0.60) |
— |
(≤0.60) |
0.20~0.60 |
Ni |
(≤0.60) |
—[TJC STEEL] |
— |
— |
Mechanical Property
Density(g/cm3)20℃ |
7.78 |
|
Melting point(℃) |
1427~1510 |
|
Specific heat [kJ/(kg·K)] 0~100℃ |
0.46 |
|
Heat conductivity [W/(m·K)][TJC STEEL] |
100℃ |
26.0 |
500℃ |
|
|
coefficient of linear expansion(10-6/K) |
0~100℃ |
10.4 |
0~500℃ |
11.4 |
|
specific resistance(Ω·mm2/m)20℃ |
0.60 |
|
longitudinal modulus of elasticity(kN/mm2)20℃ |
200 |
Steel Grade Characteristics:
Compared with 430, adding sulfur makes 430F:
(1) easier to cut, good mechanical performance;
(2) reduce the corrosion[TJC STEEL] resistance;
(3) reduced solderability.
In addition, the 430F has similar mechanical properties to the 430, as well as:
(4) can not heat treatment;
(5) with ferromagnetism;
(6)The corrosion resistance is not as good as austenite.
Applications:
430F is a widely used free [TJC STEEL]cutting stainless steel, mainly used in the manufacture of high cutting volume automatic lathe machining parts, hydraulic parts, fasteners, sanitary and durable appliances, etc.